ABSTRACT The functionalization of the PVC/Carbonate polymer system was evaluated in face of the incorporation of SBR-r rubber residues. The samples were prepared in an internal Haake-type mixer and the torque was evaluated when the residues were incorporated into the polymeric system. In the different concentrations of SBR-r studied and considering the equilibrium conditions during processing, the mixtures were characterized through physical-chemical and mechanical tests. In the FTIR spectra, it can be observed that the incorporation of the residue, even in the highest concentrations, did not change the characteristic bands of PVC/CaCO3, which may indicate that there was only physical interaction in the system. The mechanical strength was reduced with the increase in the percentage of incorporation of the rubber residue to the PVC/CaCO3 system, and a slight increase in the hardness of the composite was observed. With the increase in incorporations, there was a reduction in the crystallinity of the systems. The systems presented similar thermal behavior, with three stages of decomposition. The PVC system SBR-r-25 Ca-75 showed greater thermal stability (178 ºC). The increase in the percentage of incorporation of the SBR-r to the PVCCa caused a slight decrease in the TD10% and TD50% temperatures, however, for the TD90% this reduction was more effective. The results obtained in the fluidity of the systems, was of 93% of efficiency of the flow index, in comparison to the expected of the PVCCa100. Although the increase in the incorporation of rubber residues has indicated physical-chemical and mechanical changes in the characterizations, the results in general were quite significant, allowing in this present work an alternative for application in industrial scale of the PVC SBR- r-25 Ca-75 and PVC SBR-r-50 Ca-50.

RESUMO Avaliou-se a funcionalização do sistema polimérico PVC/Carbonato diante da incorporação de resíduos de borracha SBR-r. As amostras foram preparadas em um misturador interno do tipo Haake e avaliado o torque aos serem incorporados os resíduos no sistema polimérico. Nas diversas concentrações de SBR-r estudadas e considerando as condições de equilíbrio durante o processamento, as misturas foram caracterizadas através de ensaios físico-químicos e mecânicos. Nos espectros de FTIR, pode se observar que a incorporação do resíduo, mesmo nas maiores concentrações, não alterou as bandas características do PVC/CaCO3 o que pode indicar que houve apenas interação física no sistema. A resistência mecânica foi reduzida com o aumento no percentual de incorporação do resíduo de borracha ao sistema PVC/CaCO3, e observou-se uma discreta elevação na dureza do compósito. Com o aumento das incorporações verificou-se uma redução na cristalinidade dos sistemas. Os sistemas apresentaram comportamento térmicos semelhantes, com três etapas de decomposição. Tendo o sistema PVC SBR-r-25 Ca-75 apresentado maior estabilidade térmica (178 ºC). O aumento do percentual de incoporação do SBR-r ao PVCCa, provocou uma leve diminuição das temperaturas TD10% e TD50%, no entanto, para o TD90% essa redução foi mais efetiva. Os resultados obtidos na fluidez dos sistemas, foi de 93% de eficácia do índice de escoamento, em comparação ao esperado do PVCCa100. Embora o aumento da incorporação dos resíduos de borracha tenha indicado mudanças fisicos-químicas e mecânicas das caracterizações, os resultados de uma forma geral foram bastante significativos, possibilitando neste presente trabalho uma alternativa para aplicação em escala industrial dos sistemas PVC SBR-r-25 Ca-75 e PVC SBR-r-50 Ca-50.

Resumo Neste estudo, objetivamos caracterizar solos de três depósitos sedimentares utilizados como fontes de matéria-prima para indústrias de cerâmica localizadas no semiárido brasileiro. As amostras foram coletadas em depósitos localizados nos municípios de Barra de São Miguel, Juazeirinho e Santa Cecília, nomeadas, preparadas e submetidas a testes para determinação das características mineralógicas, químicas, físicas e térmicas pelas técnicas XRD, EDX, Casagrande, análise granulométrica, TG e DTA. As composições dos solos continham quartzo, alumina e hematita, predominantemente, cerca de 90% do total, com picos bem definidos nos difratogramas que confirmam a afirmação, e apresentaram plasticidade e distribuição médias de grãos que os encaixam como silto-argilosos. Quando aquecidas até 1000 °C, as perdas ao fogo foram de 17%, 16% e 29% para as amostras de Barra de São Miguel, Juazeirinho e Santa Cecília, percentual devido à desidratação e queima de matéria orgânica. Assim, os solos estudados atenderam aos requisitos das normas brasileiras que tratam da produção de tijolos de vedação (com sinterização) e de solo-cimento (por prensagem). Os depósitos estudados oferecem matéria-prima satisfatória para a indústria cerâmica e podem fornecer solo para a produção de tijolos solo-cimento (tijolos ecológicos).

Abstract In this study, we aimed to characterise soils of three sedimentary deposits used as raw material sources for ceramic industries located in the Brazilian semi-arid region. The samples were collected in deposits located in the cities of Barra de São Miguel, Juazeirinho and Santa Cecília. They were named, prepared and submitted to tests to determine the mineralogical, chemical, physical and thermal characteristics using the XRD, EDX, Casagrande, granulometric analysis, TG and DTA. The soils presented compositions containing quartz, alumina and hematite, predominantly with about 90% of the total, with well-defined peaks in the diffractograms confirming the statement, and averages of plasticity and granulometric distribution that fit them as silt-clay. When heated to 1000 °C, fire losses were 17%, 16% and 29% for samples from Barra de São Miguel, Juazeirinho and Santa Cecília, respectively, which is due to the dehydration and burning of organic matter. Thus, they have met the requirements of the Brazilian standards that deal to produce sealing (with sintering) and soil-cement bricks (by pressing). The studied deposits offer satisfactory raw material for the ceramics industry and can provide soil for soil-cement brick (ecological bricks) production.

RESUMO Um grande número de ligas metálicas apresenta comportamento satisfatório quando usadas na fabricação de implantes para próteses de quadril. Porém, as mesmas devem estar em conformidades com as normatizações, para assegurar sua qualidade por longos períodos e sem perder sua funcionalidade. Portanto, o presente trabalho tem como objetivo estudar as não conformidades de duas próteses de quadril, sendo uma de titânio e outra de aço inoxidável frente às normatizações. As próteses estudadas passaram por análise de difração de raios-x (DRX), fluorescência de raios-x, ensaio de tração e microscopia óptica (MO). As amostras para o ensaio de tração foram confeccionadas conforme a norma ASTM E 8M, bem como, as amostras do MO passou pelo procedimento metalográfico. Os resultados evidenciaram que algumas composições químicas apresentaram discordância em relação às normas. As análises de DRX mostraram picos de austenita e ausência de ferrita para o aço inoxidável, enquanto a liga de titânio apresenta uma fase alfa (HC) mais significativa que a fase beta (CCC). As ligas de aço inox e titânio apresentam limite de escoamento e resistência à tração que atendem as normas. Por outro lado, o módulo de elasticidade das ligas de titânio e aço inox, chega a ser dez vezes maior do que o módulo do osso humano. Portanto, o alto módulo de elasticidade das ligas, favorece problemas de reabsorção óssea. A microestrutura do aço inox é típica de uma matriz austenítica, enquanto a da liga de titânio apresenta microestruturas α+ β.

ABSTRACT A large number of metallic alloys has satisfactory behavior when used to manufacture implants for hip prostheses. However, they must be in conformity with standards, to ensure their quality for long periods without losing its functionality. Therefore, this paper aims to study the non-conformities in two hip prostheses, one of titanium and other stainless steel according to standards. The implants studied passed by x-ray diffraction (XRD), x-ray fluorescence, tensile test and optical microscopy (OM). Specimens for the tensile test were made according to ASTM E 8M, as well, MO samples passed by metallographic procedure. The results evidenced that some chemical compositions showed in relation to the standards. The XRD analysis showed peaks of austenite and absence of ferrite for the stainless steel, while the titanium alloy presents an alpha phase (HCP) more significant than the beta phase (BCC). The stainless steel alloys and titanium have yield strength and tensile strength that meet the standards. On the other hand, the elastic modulus of the titanium alloy and stainless steel, comes to be ten times greater than the human bone. Therefore, the high modulus of elasticity of the alloys, favors bone resorption problems. The stainless steel microstructure is typical of an austenitic matrix, while the titanium alloy presents α + β microstructure.